Studies on Surface Structure and Grain Coarsening in Sphere-Forming Triblock Copolymer Thin Films
http://hdl.handle.net/10212/2508
http://hdl.handle.net/10212/2508278e70d4-c7f9-4a94-af42-1a0956510585
| 名前 / ファイル | ライセンス | アクション |
|---|---|---|
内容の要約 (298.4 KB)
|
|
|
|
内容・審査結果の要旨 (196.9 KB)
|
|
| Item type | 学位論文 / Thesis or Dissertation(1) | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| 公開日 | 2021-08-26 | |||||||||
| タイトル | ||||||||||
| タイトル | Studies on Surface Structure and Grain Coarsening in Sphere-Forming Triblock Copolymer Thin Films | |||||||||
| 言語 | en | |||||||||
| その他のタイトル | ||||||||||
| その他のタイトル | 球状ミクロ相分離構造を形成するトリブロック共重合体薄膜の表面構造とグレイン成長に関する研究 | |||||||||
| 言語 | ja | |||||||||
| 作成者 |
ラシャ アハメド ハナフィ ベイヨミ
× ラシャ アハメド ハナフィ ベイヨミ
|
|||||||||
| アクセス権 | ||||||||||
| アクセス権 | open access | |||||||||
| アクセス権URI | http://purl.org/coar/access_right/c_abf2 | |||||||||
| 主題 | ||||||||||
| 言語 | en | |||||||||
| 主題Scheme | Other | |||||||||
| 主題 | Block copolymer | |||||||||
| 主題 | ||||||||||
| 言語 | en | |||||||||
| 主題Scheme | Other | |||||||||
| 主題 | thin film | |||||||||
| 主題 | ||||||||||
| 言語 | en | |||||||||
| 主題Scheme | Other | |||||||||
| 主題 | Spherical microdomains | |||||||||
| 主題 | ||||||||||
| 言語 | en | |||||||||
| 主題Scheme | Other | |||||||||
| 主題 | Free surface | |||||||||
| 主題 | ||||||||||
| 言語 | en | |||||||||
| 主題Scheme | Other | |||||||||
| 主題 | Atomic force microscopy | |||||||||
| 主題 | ||||||||||
| 言語 | en | |||||||||
| 主題Scheme | Other | |||||||||
| 主題 | X-ray photoelectron spectroscopy | |||||||||
| 主題 | ||||||||||
| 言語 | en | |||||||||
| 主題Scheme | Other | |||||||||
| 主題 | small-angle X-ray scattering | |||||||||
| 主題 | ||||||||||
| 言語 | en | |||||||||
| 主題Scheme | Other | |||||||||
| 主題 | grazing-incidence small-angle X-ray scattering | |||||||||
| 主題 | ||||||||||
| 言語 | en | |||||||||
| 主題Scheme | Other | |||||||||
| 主題 | Grain | |||||||||
| 主題 | ||||||||||
| 言語 | en | |||||||||
| 主題Scheme | Other | |||||||||
| 主題 | Hierarchical structure | |||||||||
| 主題 | ||||||||||
| 言語 | en | |||||||||
| 主題Scheme | Other | |||||||||
| 主題 | Superthin film | |||||||||
| 主題 | ||||||||||
| 言語 | en | |||||||||
| 主題Scheme | Other | |||||||||
| 主題 | dewetting | |||||||||
| 主題 | ||||||||||
| 言語 | en | |||||||||
| 主題Scheme | Other | |||||||||
| 主題 | monolayer | |||||||||
| 主題 | ||||||||||
| 言語 | en | |||||||||
| 主題Scheme | Other | |||||||||
| 主題 | islands. | |||||||||
| 内容記述 | ||||||||||
| 内容記述タイプ | Abstract | |||||||||
| 内容記述 | The thesis focuses on the triblock copolymer forming spherical microdomains. Namely, glassy spherical microdomains embed in a rubbery matrix. Although the glass transition temperature ( ) of the rubbery phase is much lower than room temperature, the polymeric as-cast film sometimes exhibits non-equilibrium characters. This is because the glassy spherical phase of which is much higher than room temperature, results in impeding the chains in the rubbery matrix phase to freely move in the as-cast state. The thesis is divided into three chapters. Chapter 1 investigates the surface structures of three kinds of block copolymers forming equilibrium and non-equilibrium spherical microdomains by using the atomic force microscopy, X-ray Photoelectron Spectroscopy, and Grazing-Incidence Small-Angle X-ray Scattering. Plausible model could be constructed based on that. The main finding of chapter 1 is that the layer thickness of the outermost surface is found to be very thin so that the block chains confined in this space are forced to be heavily compressed. Such an enormous chain deformation indicates that the surface coverage requirement is very strong. Chapter 2 presents the grain coarsening on the free surface as well as in the thickness direction of sphere-forming triblock copolymer film. The main finding of chapter 2 is that the oriented layer thickness near the free surface (or facing to the substrate) has reached 9.5 μm thick, consuming almost 20 % of the total film thickness. This value is much bigger than the reported one in the literatures. Chapter 3 addresses the ordering regularity of spherical microdomains in a dewetted triblock copolymer superthin film. The main finding of chapter 3 is that it has been found that the ordering packing inside the dewetted islands varies from a regular hexagonal to a deformed hexagonal packing, depending on the shape of the islands. | |||||||||
| 言語 | en | |||||||||
| 日付 | ||||||||||
| 日付 | 2018-09-25 | |||||||||
| 日付タイプ | Issued | |||||||||
| 言語 | ||||||||||
| 言語 | eng | |||||||||
| 資源タイプ | ||||||||||
| 資源タイプ識別子 | http://purl.org/coar/resource_type/c_db06 | |||||||||
| 資源タイプ | doctoral thesis | |||||||||
| 学位授与番号 | ||||||||||
| 学位授与番号 | 甲第906号 | |||||||||
| 学位名 | ||||||||||
| 言語 | ja | |||||||||
| 学位名 | 博士（工学） | |||||||||
| 学位授与年月日 | ||||||||||
| 学位授与年月日 | 2018-09-25 | |||||||||
| 学位授与機関 | ||||||||||
| 学位授与機関識別子Scheme | kakenhi | |||||||||
| 学位授与機関識別子 | 14303 | |||||||||
| 言語 | ja | |||||||||
| 学位授与機関名 | 京都工芸繊維大学 | |||||||||